304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm

JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm

Brand Name : DELTA

Model Number : 201 304 316L 321 309S 310S 2205 17-4PH

Certification : ISO

Place of Origin : China

MOQ : 500 kgs

Price : 2400 - 3500 USD/Ton

Payment Terms : L/C, T/T, Western Union

Supply Ability : 20Ton per week

Delivery Time : 5 - 12 days based on the quantity

Packaging Details : standard packing for export

Shape : round

Standard : ASTM EN GB JIS

Grade : 201 304 316L 309S 310S 321 2205 2507.etc

Application : Construction,Industry,surgical tools,seawater equipment.,kitchenware

Length : Customers' Requirements,5.8m,6m,2m-6m,or as required

Size : custom as request

Packing : Standard Seaworthy Package,In wooden cases(for FCL/ LCL shipment)

Service : Cutting, surface finishing

Contact Now

Grade 304 Stainless Steel Grinding Bar High Precision Stainless Steel Shaft Tolerance H5 H7 H9

Products Stainless Steel Bar
Grade 201 303 304 304L 309S 310S 316L 316Ti 317L 321 347 410 420 430 431 17-4PH 2205 2507 904L C276.etc
Finishing Bright / Black
Diameter 3 - 300mm
Tolerance H5 H6 H7 H8 H9 H10 H11 H12 H13
Length 6m or custom cutting as request
Service Cutting. Polishing, heat treatment
MOQ 200 Kgs
Deliver time 10 - 15 Days based on the quantity
Packing wooden box, or packing as request
Loading Port Shanghai Port. Ningbo Port
Other Shape Round, Square, Flatness, Hexagonal , Angle, Channel
Company Type Factory

304 is a chromium-nickel austenitic stainless steel with good strength and excellent corrosion resistance as supplied in the annealed condition with a typical brinell hardness of 175.Characterised by high corrosion resistance in general atmospheric corrosive environments it exhibits excellent resistance to most oxidizing agents, general foodstuffs, sterilizing solutions, dyestuffs, most organic chemicals, plus a wide variety of inorganic chemicals also hot petroleum gases, steam combustion gases, nitric acid and to a lesser extent sulphuric acid. It displays good oxidation resistance at elevated temperatures and has excellent weldability.

304 cannot be hardened by thermal treatment, but strength and hardness can be increased substantially by cold working, with subsequent reduction in ductility.
It is now available with improved machinability (by calcium injection treatment) which has little affect on corrosion resistance and weldability, while greatly increasing feeds and/or speeds plus extending tool life.
Used extensively by the Food Processing, Dairy Equipment, Dying Industry, Architectural Equipment, Hardware and Kitchenware Manufacturing Industry, Chemical, Petrochemical and Transport Industry etc..
Material non magnetic in the annealed condition, but can become mildly magnetic following cold working. Annealing is required to rectify if necessary.
N.B. Optimum corrosion resistance is achieved in the annealed condition.
Colour Code Stocked Sizes
Bright Green
(Bar end)
304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm
STOCKED SIZES 3mm to 350 mm diameter.
Bar Finish
Peeled, Cold Drawn
Turned and Polished, and
Centreless Ground.
Related Specifications
Australia AS 2837-1986-304
Germany W.Nr 1.4301 X5CrNi 18 10
Great Britain BS970 Part3 1991 304S15/304S31
BS970 1955 EN58E
Japan JIS G4303 SuS 304
USA ASTM A276-98b 304
SAE 30304 AISI 304
UNS S30400
Chemical Composition
Min. % Max %
Carbon 0 0.08
Silicon 0 1.00
Manganese 0 2.00
Nickel 8.00 10.50
Chromium 18.00 20.00
Nitrogen 0 0.10
Phosphorous 0 0.045
Sulphur 0 0.03
*Molybdenum option addition.
Mechanical Property Requirements - Annealed to ASTM A276-98b 304
Finish Hot Finish Cold Finish Cold Finish
Dia or Thickness mm All Up to & incl 12.7mm Over 12.7mm
Temsile Strength Mpa Min. 515 620 515
Yield Strength Mpa Min. 205 310 205
Elongation in 50mm % Min. 40 30 30
Typical Mechanical Properties At Room Temperature - Annealed
Finish Cold Drawn Other
Tensile Strength Mpa 680 590
Yield Strength Mpa 500 240
Elongation in 50mm % 42 55
Impact Charpy V J 190 183
Hardness HB 195 155
Rc 13
Elevated Temperature Properties
304 displays good oxidation resistance in continuous service up to 930 oC and in intermittent service up to 870 oC.Continuous service however, between 430 oC and 870 oC is not recommended, nor is slow cooling through this range due to the problem of intergranular corrosion. 304L (low carbon type) can be employed to overcome this problem.

Mechanical properties are reduced as temperature increases.
Typical Mechanical Properties - Annealed at Elevated Temperatures
Temperature oC 20 430 550 650 760 870
Short - Time Tensile Tests Tensile Strength Mpa 580 425 370 310 205 140
Yield Strength Mpa 240 150 130 115 95 70
Elongation in 50mm % 60 40 35 32 33 40
Creep Tests Stress for % Creep in
10,000 hours Mpa
115 50 15
Low Temperature Properties
304 has excellent low temperature properties with increased tensile and yield strength without loss of toughness in the annealed condition.
Typical Mechanical Properties - Annealed at Zero and Sub-Zero Temperatures
Temperature oC 0 -70 -130 -180 -240
Tensile Strength Mpa 870 1000 1300 1400 1650
Yield Strength Mpa 260 300 350 375 450
Elongation in 50mm % 57 50 45 40 30
Impact Charpy V J 190 190 185 180 180
The combination of high strength and toughness at low temperature allows this grade to be used in extremely cold climates or high altitudes, also for storage or liquified gasses at very low temperatures.304 even when cold worked will still have high strength and ductility at sub-zero temperatures.
Cold Bending
304 has excellent cold working properties and cold bending can generally be carried out without difficulty, after cold working it will be mildly magnetic. Annealing is generally not required except following very severe cold working.
Hot Bending
Hot bending should be performed at 950 oC - 1100 oC, followed by annealing to restore optimum corrosion resistance.
Corrosion Resistance - All Corrosion Types
General Corrosion
304 has better resistance to general corrosion in most media than 303 or 302 grades but not as good as 316 and 316L grades.
Stress Corrosion Cracking
304 has better resistance to stress corrosion cracking than 303 grade, but not as good as 316 or 316L grades.
Pitting Corrosion / Crevice Corrosion
304 has better resistance to both pitting and crevice corrosion than 303 grade but not as good as the molybdenum bearing grades 316 and 316L etc.
Intergranular Corrosion
304 has better resistance to intergranular corrosion than the higher carbon grades 303, 310 or 302, but not as good as the low carbon grades 304L and 316L, or the titanium stabilised grade 321.N.B. It is most important that oxygen is always allowed to circulate freely on all stainless steel surfaces to ensure that a chrome oxide film is always present to protect it. If this is not the case, rusting will occur as with other types of non stainless steel.

For optimum corrosive resistance, surfaces must be free of scale and foreign particles.
Finished parts should be passivated.
Forging
Heat uniformly to 1150 oC - 1200 oC, hold until temperature is uniform throughout the section.Do not forge below 900 oC

Finished forgings should be air cooled.
Finally forgings will require to be annealed in order to obtain optimum corrosion resistance.
Heat Treatment
Annealing
Heat to 1020 oC - 1100 oC, hold until temperature is uniform throughout the section. *Soak as required. Quench in water to obtain optimum corrosion resistance.*Actual soaking time should be long enough to ensure that the part is heated thoroughly throughout its section to the required temperature, 30 minutes per 25 mm of section may be used as a guide.

Please consult your heat treater for best results.
Machining
304 improved machinability is slightly more easy to machine than improved machinability 316 or 316L grades. But more difficult to machine than 303 free machining grade and most of the 400 series stainless steels. It has a typical machinability rating of around 55% - 60% of free machining (S1214) mild steel.Due to its high work hardening rate, cutting or drilling tools etc. must be kept sharp at all times and not cause unnecessary work hardening of the surface etc.

All machining should be carried out as per machine manufacturers recommendations for suitable tool type, feeds and speeds.
Welding
304 is readily weldable by shielded fusion and resistance welding processes, followed by air cooling giving good toughness. Oxyacetylene welding is not recommended due to possible carbon pick up in the weld area.Small sections may be welded without loss of corrosion resistance due to intergranular carbide precipitation, but larger sections or for service in the more extreme condition, post weld annealing is recommended.
Welding Procedure
Welding electrodes or rods should be 308 or *similar depending upon application.
No pre heat or post heat is generally required.*Please consult your welding consumables supplier.
Interlloy believes the information provided is accurate and reliable. However no warranty of accuracy, completeness or reliability is given, nor will any responsibility be taken for errors or omissions.
304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm

Product Tags:

Stainless Steel Grinding Bar

      

H9 304 Stainless Steel Grinding Bar

      

300mm Stainless Steel Grinding Bar

      
Best 304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm wholesale

304 Stainless Steel Grinding Bar High Precision Shaft Tolerance H5 H7 H9 300mm Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
*Subject:
*Message:
Characters Remaining: (0/3000)